This indicates that the flame straightening process was carried out at a temperature above 500°C, which led to the phenomenon of dechromination of areas adjacent to the

However, performance presented by super duplex stainless steels can be drastically reduced if undesirable phases, such as sigma phase, chi phase, secondary austenite and a lot of

– steel designated as 304L Mo exhibits the highest corrosion resistance in 0.1 M NaCl solution (the lowest values of corrosion rate (CR and MR) and corrosion current

The mixed microstructure causes duplex steels to combine properties of ferritic and austenitic stainless steels, for example, their resistance to stress corrosion cracking

A large difference in the temperature on the outer surface of the sheet means that the analysed device cannot be successfully used in the heating process of

Corrosion resistance of metal biomaterials (stainless steel, Ti6Al4V, Ti6Al7Nb) coated with PLGA polymer, after 90 days exposure to Ringer’s solution was

The aim of this study is to evaluate the effect of temperature on the corrosion resistance of AISI 316Ti stainless steel with chemically treated surface (nitric acid

The high corrosion resistance of the treated S32615 steel is related to the formation of thinner top layer containing amorphous and complex compounds of silicon, oxide, carbon